《工程塑料应用》 2017年第03期
DOI:10.3969/j.issn.1001-3539.2017.03.016
热处理工艺对PBO纤维拉伸性能影响
朱晓琳,钟蔚华,金子明,张鹏,虢忠仁,宫平,曲志敏
中国兵器工业集团第五三研究所,济南 250031 
Effect of Heat-Treatment Procedure on Tensile Properties of PBO Fiber by Means
Zhu Xiaolin, Zhong Weihua, Jin Ziming, Zhang Peng, Guo Zhongren, Gong Ping, Qu Zhimin
China North Industries Group Corporation Institute 53, Jinan 250031, China 
摘要:针对研究较少的聚对苯撑苯并双恶唑(PBO)纤维热处理工艺进行研究,通过控制热处理气氛、热处理温度、热处理停留时间和预加应力4个参数,对初纺丝PBO(PBO-AS)纤维的热处理工艺进行优化,得到拉伸性能大幅提高的PBO-HM纤维。利用电子织物强力仪对PBO-HM纤维的拉伸性能进行测试,发现热处理氛围为N2时PBO-HM纤维的性能更为优异;热处理温度控制在550℃以下时,热处理温度越高,热处理后得到的PBO-HM纤维的拉伸弹性模量越高,但热处理停留时间延长会使拉伸强度降低;预加应力有助于PBO-HM纤维拉伸弹性模量的增加。经分析得出,最优热处理温度为550℃,热处理停留时间为53.3 s,预加应力为5.48 cN/dtex,得到的PBO-HM的拉伸性能较优。 
Abstract:The heat treatment process of poly-p-phenylene benzobisthiazole (PBO) fibers was studied and optimized by controlling the parameters, such as heat treatment atmosphere, heat treatment temperature, heat treatment residence time and pre-stress. The tensile properties of PBO-AS fiber were greatly improved of PBO-HM fibers. The tensile strength of PBO-HM fibers were tested by electronic fabric strength meter. It can be found that PBO-HM fiber can have better properties when heat treatment atmosphere is N2. When the heat treatment temperature could be controlled below 550℃, the higher the heat treatment temperature is, the higher the modulus of PBO-HM fiber will present. But the elongation of heat treatment residence time decrease tensile strength of the PBO-HM fiber. Pre-stressing stress contributes to the increase of PBO-HM fiber tensile modulus of elasticity. The results show that the optimum heat treatment temperature can be 550℃, the heat treatment residence time is 53.3 s, the pre-stressing stress is 5.48 cN/dtex, the tensile property of PBO-HM will be more accepted. 
关键词:聚对苯撑苯并双恶唑纤维;热处理;高模量;高强度 
Keywords:poly-p-phenylene benzobisthiazole fiber; heat treatment; high modulus; high strength 
本文引用格式:
朱晓琳,钟蔚华,金子明,等.热处理工艺对PBO纤维拉伸性能影响[J].工程塑料应用,2017,45(3):73-77.
Zhu Xiaolin,Zhong Weihua,Jin Ziming,et al.Effect of heat-treatment procedure on tensile properties of PBO fiber by means[J].Engineering Plastics Application,2017,45(3):73-77. 

原文:
 
相似文章:
  热处理温度对碳纤维增强聚酰亚胺复合材料性能影响
2020年第06期
  HPMC提高Zn2+配位丙烯酸基弹性体强度和自恢复性
2020年第06期
  热处理温度对苎麻纤维增强酚醛树脂复合材料性能影响
2020年第05期
  湿热环境下的PMI泡沫材料压缩蠕变特性
2020年第02期
  BMA/AM/AA共聚物的制备
2019年第09期
  PA6/GF复合材料力学性能改进研究进展
2019年第05期
  PLA/TPEE共混物的制备及性能
2019年第06期
  小直径全氟乙烯丙烯共聚物薄壁管的热弯成型工艺
2019年第02期
  PA66产品尺寸稳定性的影响因素
2019年第01期
  热处理对PPS结晶度的影响分析
2017年第12期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5