《工程塑料应用》 2019年第09期
DOI:10.3969/j.issn.1001-3539.2019.09.002
PEDOT∶PSS的合成及二次掺杂对其导电性的影响
冯春梅1,曾明2,陈中华1,李亮1,刘文艺1,雷钰君1,胡章润1,彭娅1
1. 西华大学材料科学与工程学院,成都 610039; 2.重庆市食品药品检验所,重庆 401123 
Synthesis and the Effect of Secondary Doping on Its Electrical Conductivity of PEDOT∶PSS
Feng Chunmei1, Zeng Ming2, Chen Zhonghua1, Li Liang1, Liu Wenyi1, Lei Yujun1, Hu Zhangrun1, Peng Ya1
1. School of Materials Science and Engineering, Xihua University, Chengdu 610039, China; 2. Chongqing Food and Drug Inspection Institute, Chongqing 401123, China 
摘要:为改善聚(3,4-亚乙基二氧噻吩)(PEDOT)不溶不熔的特点,用聚苯乙烯磺酸(PSS)作为掺杂剂采用化学氧化法制备了PEDOT∶PSS复合材料。研究表明,当PEDOT∶PSS质量比=1∶3时,复合材料的溶解性最佳。在此基础上分别研究了硫酸、甲酸、乙酸作为二次掺杂剂对复合材料导电性能的影响。结果表明,二次酸掺杂的PEDOT∶PSS电导率较PEDOT∶PSS复合材料均有明显的提高,且硫酸掺杂效果远优于甲酸、乙酸,且硫酸的浓度达到8 mol/L时,PEDOT∶PSS复合材料的电导率可高达4.22 S/cm。 
Abstract:In order to improve the solubility of poly (3,4-ethylenedioxythiophene) (PEDOT), polystyrene sulfonate (PSS) was used as a dopant to prepare poly (3,4-ethylenedioxythiophene)∶polystyrene sulfonate (PEDOT∶PSS) composites by chemical oxidation method. It is revealed that the solubility of the composites has the best solubility when the ration of PEDOT∶PSS is 1∶3. On this basis, the effects of sulfuric acid, formic acid and acetic acid as secondary dopants on the conductivity of the composites were studied. It is showed that the conductivity of PEDOT∶PSS doped by secondary acid is significantly higher than that of PEDOT∶PSS and the conductivity of PEDOT∶PSS doped by sulfuric acid is much higher than that of formic acid and acetic acid. When the concentration of sulfuric acid reaches 8 mol/L, the conductivity of PEDOT∶PSS can be as high as 4.22 S/cm. 
关键词:聚(3,4-亚乙基二氧噻吩);聚苯乙烯磺酸盐;掺杂;电导率;溶解性 
Keywords:poly(3,4-ethylenedioxythiophene); polystyrene sulfonate; doping; conductivity; solubility 
基金:四川省教育厅重点项目(12ZA15),教育部“春晖计划”科研项目(Z2010093),“西华杯”大学生创新创业项目(2019050) 
本文引用格式:
冯春梅,曾明,陈中华,等. PEDOT∶PSS的合成及二次掺杂对其导电性的影响[J].工程塑料应用,2019,47(9):7-11.
Feng Chunmei,Zeng Ming,Chen Zhonghua,et al. Synthesis and the effect of secondary doping on its electrical conductivity of PEDOT∶PSS[J]. Engineering Plastics Application,2019,47(9):7-11. 

原文:
 
相似文章:
  PVDF/CaCu(3-x)MgxTi4O12复合材料制备及介电性能
2019年第08期
  硬质PMI泡沫的表面化学镀及其电磁性能
2019年第05期
  聚苯并咪唑类高温质子交换膜研究进展
2019年第06期
  nano-ATO对双层共挤PE-LD农用棚膜性能的影响
2019年第03期
  高导电PEDOT/PSS复合材料改性研究进展
2018年第08期
  电致变色器件中聚丙烯酸酯类电解质的研究
2017年第08期
  石墨烯掺杂聚苯胺导电复合材料的研究进展
2013年第11期
  新型功能性聚酰亚胺的研究与应用进展
2013年第01期
  含三氟甲基聚芳醚酮的合成与表征
2012年第01期
  PA6/聚苯胺复合材料的研制
2010年第08期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5