《工程塑料应用》 2019年第09期
DOI:10.3969/j.issn.1001-3539.2019.09.003
碳纳米管改性PA6复合材料的制备与性能
阳范文1,欧阳阅翰2,沈佳豪1,孙书情1,柳蔚洲2,李荣荣1,徐蒙蒙1,陈安鸿1,田秀梅1,陈晓明1
1.广州医科大学基础医学院生物医学工程系,广州 511436; 2.广州市第六中学,广州 510300 
Preparation and Properties of PA6 Composite Modified by Carbon Nanotubes
Yang Fanwen1, Ouyang Yuehan2, Shen Jiahao1, Sun Shuqing1, Liu Weizhou2, Li Rongrong1, Xu Mengmeng1,
1. Department of Biomedical Engineering, School of Basic Medical Sciences, Guangzhou Medical University, Guangzhou 511436, China; 2. Guangzhou No.6 Middle School, Guangzhou 510300, China 
摘要:以YY-702为增容偶联改性剂,采用熔融共混方法分别制备尼龙(PA)6/碳纳米管(CNTs)-10,PA6/CNTs-5复合材料,系统研究了YY-702用量对复合材料的熔体流动速率(MFR)、力学性能和热力学行为的影响。结果表明,随着YY-702含量增加,PA6/CNTs复合材料的拉伸强度呈上升趋势;当YY-702质量分数分别为3%和4%时,PA6/CNTs-10,PA6/CNTs-5复合材料的拉伸强度达到最大值,分别为72.2 MPa和75.8 MPa。随着YY-702含量的增加,复合材料的MFR逐渐降低,当YY-702质量分数≥3%时,MFR基本保持不变,添加CNTs-5的MFR相对较小。差示扫描量热分析表明,对于PA6/CNTs-10和PA6/CNTs-5两种复合材料,当YY-702质量分数分别小于3%和4%时,熔融曲线和结晶曲线均未出现YY-702的熔融峰和结晶峰;而继续增大用量后分别在152.3℃和150.4℃处出现较为明显的YY-702的熔融峰。YY-702对PA6/CNTs-10和PA6/CNTs-5产生了较好的增容偶联效果,最佳用量分别为3%和4%。 
Abstract:Polyamide(PA)6/CNTs-10 and PA6/CNTs-5 blends were prepared by melt blending with YY-702 as compatibilization and coupling modifier. The effects of YY-702 content on melt index, mechanical properties and thermodynamic behavior of the blends were systematically studied. The results show that tensile strength of PA6/CNTs composites increase with the increase of YY-702 content, and the melt flow index decreases gradually. When the mass fraction of YY-702 is 3%, the tensile strength of PA6/CNTs-10 blends reaches the maximum value of 72.2 MPa, and when the amount of YY-702 is 4%, the tensile strength of PA6/CNTs-5 blends reach the maximum value of 75.8 MPa. When the content of YY-702 is greater than or equal to 3%, the melt flow index remain basically unchanged, and the melt flow index of CNTs-5 is relatively small. For the blends of PA6/CNTs-10 and PA6/CNTs-5, when the dosage of YY-702 is less than 3% and 4% respectively, the melting and crystallization peaks of YY-702 are not found on the corresponding curve. The melt peaks of YY-702 were observed at 152.3℃ (in the PA6/CNTs-10 system) and 150.4℃ (in the PA6/CNTs-5 system), respectively. Generally speaking, YY-702 produces good compatibilization and coupling effects on PA6/CNTs-10 and PA6/CNTs-5 blends, the optimum dosage is 3% (in the PA6/CNTs-10 system) and 4% (in the PA6/CNTs-5 system), respectively. 
关键词:尼龙6;碳纳米管;改性;力学性能;结晶行为 
Keywords:polyamide 6; carbonnanotubes; modify; mechanical property; crystallization 
基金:广州市高校创新创业教育平台建设重点项目(201709P05),2019年度广东省攀登计划项目(pdjh2019b0399),2018年度广东省本科高校创新创业教改项目(2018A073856) 
本文引用格式:
阳范文,欧阳阅翰,沈佳豪,等.碳纳米管改性PA6复合材料的制备与性能[J].工程塑料应用,2019,47(9):12-16,27.
Yang Fanwen,Ouyang Yuehan,Shen Jiahao,et al. Preparation and properties of PA6 Composite modified by carbon nanotubes[J]. Engineering Plastics Application,2019,47(9):12-16,27. 

原文:
 
相似文章:
  聚烯烃高值化改性及其应用研究进展
2019年第09期
  碳酸钙协同海藻酸(盐)改性PLA复合材料的制备及性能
2019年第09期
  不同水环境下碳纤维增强EP复合材料的吸湿老化
2019年第09期
  基于微纳层叠技术制备(APP+PUR-T)/PUR-T交替多层阻燃材料的结构与性能
2019年第09期
  碳纤维中空织物增强树脂基复合材料导热性能与应用
2019年第09期
  BMA/AM/AA共聚物的制备
2019年第09期
  聚酯-聚醚型聚氨酯的制备及性能
2019年第09期
  纳米SiO2对环氧树脂微胶囊填充型自修复材料的性能影响
2019年第08期
  低密度芳纶纸蜂窝制备及力学性能
2019年第08期
  增材制造用PLA/连续碳纤复合材料力学性能
2019年第08期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5