《工程塑料应用》 2019年第09期
DOI:10.3969/j.issn.1001-3539.2019.09.005
硬质PUR/膨胀蛭石复合保温材料的制备与性能
宋伟杉,王明杰,刘士瑞,陈瑶,高建民
北京林业大学木质材料科学与应用教育部重点实验室,北京 100083 
Preparation and Properties of Rigid Polyurethane/Expanded Vermiculite Composite Thermal Insulation Material
Song Weishan, Wang Mingjie, Liu Shirui, Chen Yao, Gao Jianmin
MOE Key Laboratory of Wooden Materials Science and Application, Beijing Forestry University, Beijing 100083, China 
摘要:采用一步法制备硬质聚氨酯(PUR)/膨胀蛭石(EM)复合保温材料,探讨了EM不同粒径(0.5~1 ,1~3,3~6 mm)以及不同填充比(5%,10%,20%,30%)对复合材料性能的影响。结果表明,EM的添加显著提高了硬质PUR/EM复合材料的压缩性能,当加入10%粒径为3~6 mm的EM时复合材料的压缩强度由0.12 MPa提高到0.36 MPa;随着粒径和填充比的增大,复合材料密度增大,泡孔直径减小;热导率低于0.05 W/(m·K)。当加入5%的粒径为1~3 mm的EM时,复合材料的热导率低至0.029 W/(m·K)。EM的添加提高了复合材料的阻燃效果,当加入30% EM (3~6 mm)时,极限氧指数增加了15%达到21.1%。 
Abstract:Rigid polyurethane/expanded vermiculite composite insulation materials were prepared by one-step method. The effects of different particle sizes (0.5-1 mm, 1-3 mm, 3-6 mm) and filling ratios (5%, 10%, 20%, 30%) of expanded vermiculite on the properties of the composite were discussed. The results show that the compressive strength of composites increase from 0.12 MPa to 0.36 MPa when 10% of the expanded vermiculite (3-6 mm) are added. With the increase of particle size and filling ratio, the density of composite increase and the cell diameter decrease, and the thermal conductivity are lower than 0.05 W/(m·K). When 5% expanded vermiculite (1-3 mm) are added, the thermal conductivity of the composite are as low as 0.029 W/(m·K). The addition of expanded vermiculite improved the flame retardancy of the composites. When 30% expanded vermiculite (3-6 mm) are added, the LOI of composites increase by 15% to 21.1%. 
关键词:膨胀蛭石;硬质聚氨酯;复合保温材料;压缩强度;阻燃性能 
Keywords:expanded vermiculite; rigid polyurethane; composite insulation material; compressive strength; flame retardancy 
基金:北京市自然科学基金面上项目(6192020) 
本文引用格式:
宋伟杉,王明杰,刘士瑞,等.硬质PUR/膨胀蛭石复合保温材料的制备与性能[J].工程塑料应用,2019,47(9):22-27.
Song Weishan,Wang Mingjie,Liu Shirui,et al. Preparation and properties of rigid polyurethane/expanded vermiculite composite thermal insulation material[J]. Engineering Plastics Application,2019,47(9):22-27. 

原文:
 
相似文章:
  基于微纳层叠技术制备(APP+PUR-T)/PUR-T交替多层阻燃材料的结构与性能
2019年第09期
  钛酸酯改性聚磷酸铵阻燃PP/PUR-T复合材料的性能
2019年第07期
  一种DOPO衍生物合成及其对PLA阻燃性能的影响
2019年第05期
  新能源汽车电池包上盖专用阻燃聚丙烯的研制
2019年第05期
  勃姆石/MPP二元协效AlPi阻燃PA66/GF复合材料研究
2019年第06期
  多壁碳纳米管表面羧基化及其阻燃ABS性能
2019年第03期
  磷氮膨胀型改性水滑石阻燃剂的制备及其阻燃ABS复合材料的性能
2019年第01期
  EG与GF改性聚氨酯保温材料的阻燃及力学性能
2018年第11期
  纳米OMMT与DOPO衍生物协同阻燃环氧树脂
2018年第07期
  夹层结构用泡沫芯材的耐水性能
2018年第04期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5