《工程塑料应用》 2019年第09期
DOI:10.3969/j.issn.1001-3539.2019.09.012
基于微纳层叠技术制备(APP+PUR-T)/PUR-T交替多层阻燃材料的结构与性能
张超1,石美浓1,张有忱1,焦志伟1,杨卫民1,杨利平2
1.北京化工大学机电工程学院,北京 100029; 2.广东海湾新材料研究所,广东深圳 518172 
Structure and Properties of (APP+PUR-T)/PUR-T Alternative Multilayer Flame Retardant Based on Microlayer Coextrusion Technology
Zhang Chao1, Shi Meinong1, Zhang Youchen1, Jiao Zhiwei1, Yang Weimin1, Yang Liping2
1. Mechanical and Electrical Engineering, Beijing University of Chemical Technology, Beijing 100029, China; 2. Guangdong Gulf New Materials Institute, Shenzhen 518172, China 
摘要:利用微纳层叠技术制备聚磷酸铵(APP)+热塑性聚氨酯(PUR-T)/PUR-T交替多层复合材料,通过扫描电子显微镜(SEM)、热重(TG)分析、极限氧指数(LOI)测试、垂直燃烧测试(UL 94)、万能试验机等对材料进行表征并分析其内在结构与性能的关系。结果表明,相比于传统的普通共混制备技术,微纳层叠挤出技术可以使APP在PUR-T基体中的分散性大大提高,从而提高整体材料的阻燃性能和热稳定性,当APP质量分数为15%时,通过微纳层叠挤出技术制备的复合材料的垂直燃烧达到UL 94 V-0级,LOI达到29.1%;同时微纳层叠挤出技术还可以有效地抑制传统普通共混方法中由于填料增加而导致的力学性能下降的负面影响。 
Abstract:The (APP+PUR-T)/PUR-T alternating multilayer composite was prepared by microlayer coextrusion technique.The internal structure and properties of samples were characterized and analyzed by scanning electron microscopy (SEM), thermogravimetric analysis (TGA), limiting oxygen index test (LOI), vertical burning test (UL94), universal testing machine, et al. The results show that the dispersibility of APP in the PUR-T matrix can be greatly improved by microlayer coextrusion technology compared to conventional blended technology, thereby improving the flame retardancy and thermal stability of the overall material.When the APP content is 15%, the composite material prepared by microlayer coextrusion technology reaches UL94 V-0 level, and the limiting oxygen index reaches 29.1%. At the same time, the microlayer coextrusion technology can effectively suppress the negative influence of the mechanical properties degradation caused by the increase of the filler in the conventional blended composites. 
关键词:微纳层叠挤出;复合材料;阻燃性能;力学性能 
Keywords:microlayer coextrusion technology; composite; flame retardant property; mechanical property 
基金:国家重点研发计划项目(2016YFB0302000),广东省科技计划项目(2016B090915001) 
本文引用格式:
张超,石美浓,张有忱,等.基于微纳层叠技术制备(APP+PUR-T)/PUR-T交替多层阻燃材料的结构与性能[J].工程塑料应用,2019,47(9):62-67.
Zhang Chao,Shi Meinong,Zhang Youchen,et al. Structure and properties of (APP+PUR-T)/PUR-T alternative multilayer flame retardant based on microlayer coextrusion technology[J]. Engineering Plastics Application,2019,47(9):62-67. 

原文:
 
相似文章:
  低温等离子体处理芳纶复合材料界面性能研究进展
2020年第06期
  纤维增强复合材料薄壁件轴向压缩吸能性研究进展
2020年第06期
  基于聚维酮碘改性的抗菌复合材料的研究进展
2020年第06期
  非热压罐成型法制备杂环芳纶纤维增强环氧复合材料
2020年第06期
  热处理温度对碳纤维增强聚酰亚胺复合材料性能影响
2020年第06期
  大口径复合材料天线反射面整体成型工艺研究
2020年第06期
  增容剂种类对PC/ABS合金材料适用环境的影响
2020年第06期
  聚丙烯/硬脂酸锌/纳米氧化锌发泡材料的制备
2020年第06期
  碳纳米管含量对聚酰亚胺/碳纤维复合材料性能的影响
2020年第05期
  碳纳米管改性环氧树脂/碳纤维复合材料的界面性能
2020年第05期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5