二硫化钨改性摩擦摆支座PTFE材料的力学性能
洪迪甫12,赵桂峰23,马玉宏12,朱震阳23
1.广州大学工程抗震研究中心,广州 510405; 2.工程抗震减震与结构安全教育部重点实验室,广州 510405; 3.广州大学土木工程学院,广州 510006 
Mechanical Properties of PTFE Material Modified with WS2 in Friction Pendulum Bearing
Hong Difu12, Zhao Guifeng23, Ma Yuhong12, Zhu Zhenyang23
1. Earthquake Engineering Research & Test Center, Guangzhou University, Guangzhou 510405, China; 2. Key Laboratory of Earthquake Resistance, Earthquake Mitigation and Structural Safety, Ministry of Education, Guangzhou 510405, China; 3. School of Civil Engineering, Guangzhou University, Guangzhou 510006, China 
摘要:针对摩擦摆支座聚四氟乙烯(PTFE)材料耐磨性差的问题,利用二硫化钨(WS2)填充改性PTFE,开展了拉伸性能、硬度等相关试验来分析复合材料的各项基本力学性能。结果显示,随着微米级和纳米级WS2含量的增加,拉伸强度和断裂伸长率会减小,硬度和密度会增大,耐压缩变形能力会提高;WS2含量的多少对复合材料密度影响较大,而粒径大小对其影响不大;采用微米级与纳米级含量为2%,4%,6%的WS2填充改性PTFE板在一定程度上减小了由于上部荷载作用而产生的压缩变形,提高了PTFE材料的耐磨性能,采用微米级含量为2%和纳米级含量为6%的WS2来改善摩擦滑移材料,耐压缩变形能力会更好,从而可以更好地改善摩擦滑移材料磨耗性能。研究结果可为改善摩擦摆支座的性能提供依据。 
Abstract:At present, the wear-resistance of polytetrafluoroethylene (PTFE) in friction pendulum bearing is poor, so PTFE was modified by filling with tungsten disulfide (WS2). The basic mechanical properties of the composites were analyzed through the related tests such as tensile properties and hardness. The results show that with the increase of the content of micron and nano-WS2, the tensile strength and elongation at break decrease, the hardness and density increase, and the ability to resist to compressive deformation increases. The content of WS2 has a great influence on the density of the composites, but the particle size has little effect on it. The modified PTFE plate with 2%, 4% and 6% contents of micron and nano-WS2 can reduce the compressive deformation caused by the upper load, which can improve the wear-resistance property of the PTFE material. The modified PTFE plate with 2% content of micron-WS2 and 6% content of nano-WS2 can improve the ability of composite to resist to compressive deformation better, and the wear-resistance property of PTFE slip material can be improved better. The research results can provide a basis for improving the performance of friction pendulum bearings. 
关键词:二硫化钨;聚四氟乙烯;基本力学性能;摩擦摆支座 
Keywords:tungsten disulfide; polytetrafluoroethylene; basic mechanical property; friction pendulum bearing 
基金:国家自然科学基金项目(51678173,51578170,51878196),长江学者和创新团队发展计划项目(IRT13057),广东省自然科学基金项目(2017A030313298),广州市科技计划项目(201707010295) 
本文引用格式:
洪迪甫,赵桂峰,马玉宏,等.二硫化钨改性摩擦摆支座PTFE材料的力学性能[J].工程塑料应用,2019,47(10):36-41.
Hong Difu,Zhao Guifeng,Ma Yuhong,et al. Mechanical properties of PTFE material modified with WS2 in friction pendulum bearing[J]. Engineering Plastics Application,2019,47(10):36-41. 

原文:
 
相似文章:
  PTFE中空纤维微孔膜制备工艺及应用研究进展
2020年第07期
  低吸水率和低介电损耗PTFE/SiO2复合材料制备
2020年第07期
  不同固体润滑填料对聚四氟乙烯性能的影响
2020年第06期
  聚酰亚胺填充聚四氟乙烯密封材料的性能
2019年第11期
  PTFE改性研究进展
2019年第06期
  二硫化钼填充PTFE蠕变性能
2019年第03期
  超高分子量聚乙烯复合材料的消声性能研究
2019年第03期
  密封用PTFE复合材料的压缩蠕变性能
2019年第02期
  PTFE/Al/Al2O3反应材料的力学性能与反应特性
2018年第12期
  基于正交设计的PEEK基复合材料摩擦学性能
2018年第11期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5