《工程塑料应用》 2019年第12期
DOI:10.3969/j.issn.1001-3539.2019.12.002
PEG-HA-PAA多孔型高吸水树脂的制备及性能
李鑫1,牛育华2,赵冬冬12
1.西京学院,西安 710123; 2.陕西科技大学教育部轻化工助剂化学与技术重点实验室,西安 710021 
Preparation and Properties of PEG-HA-PAA Superabsorbent Resin with Porous Structure
Li Xin1, Niu Yuhua2, Zhao Dongdong12
1. Xijing University, Xi'an 710123, China; 2. Key Laboratory of Chemistry and Technology for Light Chemical Industry, Ministry of Education, Shaanxi University of Science and Technology, Xi'an 710021, China 
摘要:选用腐殖酸(HA)为基体,采用化学发泡制孔法,以聚乙二醇(PEG)8000为致孔剂,丙烯酸(AA)为单体,过硫酸铵为引发剂,N,N-亚甲基双丙烯酰胺为交联剂,制备PEG-HA-PAA多孔高吸水树脂,研究了HA和PEG含量对PEG-HA-PAA吸水性能的影响,同时研究了PEG-HA-PAA对染料的吸附性能。结果表明,合成的高吸水树脂微观表面呈现多孔结构,具有良好的热稳定性和吸附性能。当HA和PEG含量分别为单体AA质量的12%和10%时,树脂的吸蒸馏水能力和吸盐水倍率最高,分别为791 g/g和88 g/g,对阳离子染料的吸附率均可达90%以上。 
Abstract:PEG-HA-PAA superabsorbent resin with porous structure was prepared by chemical foaming method using humic acid (HA) as matrix, neutral acrylic acid (AA) as monomer and polyethylene glycol (PEG) 8000 as pore forming agent, N,N-methylenebisacrylamide and ammonium persulfate were used as crosslinker and initiator, respectively. The effects of HA and PEG contents on the water absorbing performance of PEG-HA-PAA were studied and the adsorption of dyes by PEG-HA-PAA was also studied. The results show that the superabsorbent resin has the surface of micro porous structure, good heat resistance and absorbing performances. When HA content is 12% of AA mass and PEG content is 10% of AA mass, the resin has best distilled water capacity and salt water absorbing performance with distilled water rate and salt water rate as high as 791 g/g and 88 g/g, and the adsorption rates for cationic dyes are over 90%. 
关键词:聚乙二醇;腐殖酸;高吸水树脂;多孔结构 
Keywords:polyethylene glycol; humic acid; superabsorbent resin; porous structure 
基金:陕西省科协“学会助力创新驱动发展计划”项目(3408),西安市科技局农业科技创新工程项目[201806116YF04NC12(6)],西京学院校级科研基金项目(XJ70127) 
本文引用格式:
李鑫,牛育华,赵冬冬.PEG-HA-PAA多孔型高吸水树脂的制备及性能[J].工程塑料应用,2019,47(12):7-13.
Li Xin,Niu Yuhua,Zhao Dongdong. Preparation and properties of PEG-HA-PAA superabsorbent resin with porous structure[J]. Engineering Plastics Application,2019,47(12):7-13. 

原文:
 
相似文章:
  低含量增塑剂PEG对PLA性能的影响
2019年第12期
  超声对PMAA/PEG水凝胶的pH敏感性的影响
2019年第09期
  退火对PLA/GNPs/PEG复合材料性能的影响
2019年第05期
  p-GO/PEG复配成核剂对PLA热及力学性能的影响
2019年第01期
  氢氧化镁表面改性及在高密度聚乙烯中的应用
2018年第07期
  HA-PAA-CMC高吸水性树脂的制备及性能
2018年第07期
  细菌纤维素-聚乙二醇复合膜的制备与性能
2018年第06期
  聚乙二醇定形相变材料的热稳定性
2016年第10期
  AM-g-CCMC树脂的制备及其吸附性能
2016年第09期
  PEG400含量对PVDF膜形貌以及结晶的影响
2015年第01期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5