《工程塑料应用》 2019年第12期
DOI:10.3969/j.issn.1001-3539.2019.12.005
石墨烯-硅藻土改性PP复合材料的导电性能与力学性能
武卫莉12,李响1,陈丰雨1
1.齐齐哈尔大学材料科学与工程学院,黑龙江齐齐哈尔 161006; 2.黑龙江省高校聚合物复合改性重点实验室,黑龙江齐齐哈尔 161006 
Conductivity and Mechanical Properties of Graphene-Diatomite Modified Polypropylene Composites
Wu Weili12, Li Xiang1, Chen Fengyu1
1. College of Materials Science and Engineering, Qiqihar University, Qiqihar 161006, China; 2. Key Laboratory of Polymer Composition and Modification, College of Heilongjiang Province, Qiqihar 161006, China 
摘要:为了提高聚丙烯(PP)的导电性能,采用硅藻土包覆石墨烯改性PP复合材料,通过高阻计、力学性能测试、热重分析和差示扫描量热分析对复合材料的性能进行测试与表征。结果表明,当石墨烯的添加量为0.1份、硅藻土的添加量为0.2份时,改性PP表面电阻由纯PP的6.01×1011 Ω降低到3.68×104 Ω,体积电阻率由未加石墨烯时的7.45×1012 Ω·m降低到6.7×105 Ω·m,改性后PP的拉伸强度和冲击强度由未加石墨烯时的16 MPa和80.7 kJ/m2升高到22.7 MPa和97.3 kJ/m2。在加入0.2份硅藻土和0.1份石墨烯后,PP的热稳定性得到改善,初始分解温度提高了44℃。 
Abstract:In order to improve the conductivity of polypropylene (PP) material, the PP composites, were modified by using diatomite-coated graphene, and characterized by high resistance meter, mechanical properties tests, thermogravimetric analysis and differential scanning calorimetry. The results show that when the quantity of graphene is 0.1 phr, diatomite content is 0.2 phr, the surface resistance of modified PP is decreased from 6.01×1011 Ω of pure PP to 3.68×104 Ω, the volume resistivity is reduced from 7.45×1012 Ω·m (without graphene) to 6.7×105 Ω·m, the tensile strength and impact strength of the modified PP were increased from 16 MPa and 80.7 kJ/m2 (without graphene) to 22.7 MPa and 97.3 kJ/m2 respectively. After adding 0.2 phr diatomite and 0.1 phr graphene, the thermal stability of PP is improved, and the initial decomposing temperature is increased by 44℃. 
关键词:聚丙烯;石墨烯;硅藻土;导电复合材料;表面电阻;体积电阻率 
Keywords:polypropylene; graphene; diatomite; conductive composite; surface resistance; volume resistivity 
基金:黑龙江省省属高等学校基本科研业务费科研项目(YSTSXK201864) 
本文引用格式:
武卫莉,李响,陈丰雨.石墨烯-硅藻土改性PP复合材料的导电性能与力学性能[J].工程塑料应用,2019,47(12):27-31.
Wu Weili,Li Xiang,Chen Fengyu. Conductivity and mechanical properties of graphene-diatomite modified polypropylene composites[J].Engineering Plastics Application,2019,47(12):27-31. 

原文:
 
相似文章:
  聚丙烯/硬脂酸锌/纳米氧化锌发泡材料的制备
2020年第06期
  汽车内饰用聚丙烯复合材料制备与性能
2020年第06期
  低收缩、低线性膨胀系数聚丙烯材料研究
2020年第06期
  氧化石墨烯包覆羟基氧化铁协同增强环氧树脂的断裂韧性
2020年第06期
  极性润滑剂对滑石粉填充PP性能的影响
2020年第05期
  注塑工艺对GFPP/可膨胀微球发泡制件收缩率的影响
2020年第05期
  玻纤增强聚丙烯抗菌防霉复合材料制备及性能
2020年第05期
  耐紫外高灼热丝阻燃聚丙烯材料制备及性能
2020年第05期
  空心玻璃微珠对聚丙烯酸水凝胶溶胀性能的影响
2020年第05期
  聚合受阻胺对膨胀阻燃聚丙烯性能影响
2020年第04期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5