《工程塑料应用》 2019年第12期
DOI:10.3969/j.issn.1001-3539.2019.12.006
OMMT对PP/IFR/OMMT复合材料性能的影响
田琴12,罗继勇23,张道海24,严伟1,王奎1,秦舒浩23
1.贵阳学院,贵阳 550005; 2.国家复合改性聚合物材料工程技术研究中心,贵阳 550014; 3.贵州大学,贵阳 550025; 4.贵州民族大学,贵阳 550025 
Effects of OMMT on Properties of PP/IFR/OMMT Composites
Tian Qin12, Luo Jiyong23, Zhang Daohai24, Yan Wei1, Wang Kui1, Qin Shuhao23
1. Guiyang University, Guiyang 550005, China; 2. National Engineering Research Center for Compounding and Modification of Polymeric Materials, Guiyang 550014, China; 3. Guizhou University, Guiyang 550025, China; 4. Guizhou Minzu University, Guiyang 550025, China 
摘要:以膨胀型阻燃剂(IFR)为主阻燃剂、有机蒙脱土(OMMT)为协效剂对聚丙烯(PP)进行阻燃改性,并借助水平-垂直燃烧仪、极限氧指数(LOI)测定仪、锥形量热仪、万能试验机、冲击试验机和热重分析仪研究了纯PP及PP/IFR,PP/IFR/OMMT复合材料的阻燃性能、力学性能和热稳定性。结果表明,IFR质量分数为18%时PP/IFR复合材料的阻燃等级可达V-1级且材料的热释放速率(HRR),HRR峰值(PHRR)和总释放热(THR)较纯PP下降显著,在阻燃剂总质量分数为18%的情况下添加OMMT后PP/IFR/OMMT复合材料的阻燃等级达到V-0级且HRR,PHRR,THR值进一步降低。当OMMT质量分数为1%时,PP/IFR/OMMT复合材料的LOI最大,为31.4%,且热稳定性最佳,但过多的OMMT降低了PP/IFR/OMMT复合材料的热稳定性。当OMMT质量分数为1%和2%时,PP/IFR/OMMT复合材料的弯曲弹性模量高于纯PP。 
Abstract:Polypropylene (PP) was modified with intumescent flame retardant (IFR) as main flame retardant and organic montmorillonite (OMMT) as synergist. The flame retardant properties, mechanical properties and thermal stability of pure PP, PP/IFR composite and PP/IFR/OMMT composites were studied by horizontal-vertical burner, limiting oxygen index (LOI) test, cone calorimeter, universal tester, impact tester and thermogravimetric (TG) analysis. The results show that the flame retardant grade of PP/IFR composite reaches V-1 when the IFR content is 18wt% and the heat release rate (HRR), peak HRR (PHRR), total heat release (THR) of the composite decrease obviously compared with pure PP. When the total content of the flame retardants is 18wt%, the flame retardant grade of the PP/IFR/OMMT composite reaches V-0 and the HRR, PHRR and THR values are further reduced after adding OMMT. When the OMMT content is 1wt%, the LOI value of PP/IFR/OMMT composite is the maximum at 31.4% and the thermal stability is best, but excessive OMMT reduces the thermal stability of PP/IFR/OMMT composites. When the OMMT content is 1wt% or 2wt%, the flexural modulus of the PP/IFR/OMMT composite is higher than that of pure PP. 
关键词:有机蒙脱土;膨胀型阻燃剂;聚丙烯;复合材料;锥形量热仪 
Keywords:organic montmorillonite; intumescent flame retardant; polypropylene; composite; cone calorimeter 
基金:贵州省科技计划项目(黔科合成果[2019]4022号),2019年度贵阳市科学技术局–贵阳学院科技专项资金项目(GYU-KYZ〔2019-2020〕PT24-08) 
本文引用格式:
田琴,罗继勇,张道海,等. OMMT对PP/IFR/OMMT复合材料性能的影响[J].工程塑料应用,2019,47(12):32-36.
Tian Qin,Luo Jiyong,Zhang Daohai,et al. Effects of OMMT on properties of PP/IFR/OMMT composites[J]. Engineering Plastics Application,2019,47(12):32-36. 

原文:
 
相似文章:
  低温等离子体处理芳纶复合材料界面性能研究进展
2020年第06期
  纤维增强复合材料薄壁件轴向压缩吸能性研究进展
2020年第06期
  基于聚维酮碘改性的抗菌复合材料的研究进展
2020年第06期
  非热压罐成型法制备杂环芳纶纤维增强环氧复合材料
2020年第06期
  热处理温度对碳纤维增强聚酰亚胺复合材料性能影响
2020年第06期
  大口径复合材料天线反射面整体成型工艺研究
2020年第06期
  聚丙烯/硬脂酸锌/纳米氧化锌发泡材料的制备
2020年第06期
  汽车内饰用聚丙烯复合材料制备与性能
2020年第06期
  低收缩、低线性膨胀系数聚丙烯材料研究
2020年第06期
  极性润滑剂对滑石粉填充PP性能的影响
2020年第05期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5