《工程塑料应用》 2019年第12期
DOI:10.3969/j.issn.1001-3539.2019.12.009
基于工艺参数在线监测的聚乳酸生物塑料注射成型机理
陈金伟12,郑海仪1,梁钊发1,张绮琪1,苏似鑫1,温建强1
1.广东轻工职业技术学院轻化工技术学院,广州 510300; 2.广东轻工职业技术学院广东高校高分子材料加工工程技术开发中心,广州 510300 
Injection Molding Mechanism of PLA Bioplastics Based on Online Monitoring of Processing Parameters
Chen Jinwei12, Zheng Haiyi1, Liang Zhaofa1, Zhang Qiqi1, Su Shixin1, Wen Jianqiang1
1. College of Light Chemical Technology, Guangdong Industry Polytechnic, Guangzhou 510300, China; 2. Guangdong Polymer Material Processing Engineering Technology Development Center, Guangdong Industry Polytechnic, Guangzhou 510300, China 
摘要:利用自主搭建的工艺参数在线监测平台系统研究了熔体压力、熔体温度及注射速度等注射成型工艺参数对聚乳酸(PLA)生物塑料试样拉伸强度的影响规律,利用差示扫描量热仪和扫描电子显微镜等测试表征手段研究了不同工艺状态条件下PLA试样结构的变化规律,总结了熔体压力、熔体温度、注射速度与PLA试样力学性能、结构之间的作用机理。结果表明,在实验条件范围内,PLA试样成型时存在一个最佳工艺状态,即熔体温度180℃、熔体压力8 MPa、注射速度为注塑机最大注射速度的40%,在该状态下所成型试样的拉伸强度达到最佳;PLA成型过程的结晶存在一个由熔体压力所引发的最佳诱导结晶应力;对比熔体温度和熔体压力,注射速度是影响PLA结晶形貌的不敏感工艺参数。 
Abstract:The influences of injection molding process parameters such as melt pressure, melt temperature and injection speed on the tensile strength of bioplastics such as polylactic acid (PLA) products were studied systematically based on the self built online monitoring platform of process parameters. The change rule of PLA product structure under different process conditions was studied by using DSC, SEM. The interaction mechanism between the melt pressure, melt temperature, injection speed and mechanical properties, structure of PLA products was summarized. The results show that there is an optimal processing condition for PLA products in the range of experimental conditions, that is, the melt temperature is 180℃, the melt pressure is 8 MPa, and the injection speed is 40% of maximum injection speed of injection machine, under which the tensile strength of PLA is the best. There is an optimal induced crystallization stress caused by melt pressure in the crystallization of PLA products, and the injection speed is the insensitive process parameters affecting the PLA crystal morphology comparing with the melt temperature and melt pressure. 
关键词:工艺参数在线监测;聚乳酸;注射成型机理 
Keywords:online monitoring of process parameters; polylactic acid; injection molding mechanism 
基金:广东轻工职业技术学院2017年科技成果培育项目(KJPY002),广东轻工职业技术学院2017年拔尖人才自选项目(IB040103 
本文引用格式:
陈金伟,郑海仪,梁钊发,等.基于工艺参数在线监测的聚乳酸生物塑料注射成型机理[J].工程塑料应用,2019,47(12):50-55.
Chen Jinwei,Zheng Haiyi,Liang Zhaofa,et al. Injection molding mechanism of PLA bioplastics based on online monitoring of processing parameters[J]. Engineering Plastics Application,2019,47(12):50-55. 

原文:
 
相似文章:
  FDM 3D打印工艺参数对PLA制件力学性能的影响
2020年第01期
  不同增韧剂对PLA/稻壳木塑复合材料力学性能影响
2020年第01期
  聚乳酸/聚乙醇酸共混合金界面改性研究
2020年第01期
  聚乳酸/纳米羟基磷灰石/脱胶蚕丝纤维多孔支架的制备与性能
2019年第12期
  低含量增塑剂PEG对PLA性能的影响
2019年第12期
  PLA/PBAT共混体系的制备与性能
2019年第11期
  PUR-T协同CNF对PLA结晶及力学性能的影响
2019年第11期
  联合工艺对聚乳酸/椰壳复合材料力学性能的影响
2019年第10期
  挤出3D打印PLA/CF复合材料的力学性能
2019年第10期
  碳酸钙协同海藻酸(盐)改性PLA复合材料的制备及性能
2019年第09期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5