《工程塑料应用》 2019年第12期
DOI:10.3969/j.issn.1001-3539.2019.12.011
连续玻纤增强PP复合PET泡沫夹芯板的模压成型工艺
袁杰,李丽,徐光磊,王杏哲,刘博
山东格瑞德集团有限公司,山东德州 253000 
Compression Molding Process for Continuous Glass Fiber Reinforced PP Composite PET Foam Sandwich Panel
Yuan Jie, Li Li, Xu Guanglei, Wang Xingzhe, Liu Bo
Shandong Grad Group Co. Ltd., Dezhou 253000, China 
摘要:采用模压成型工艺,制备连续玻璃纤维(GF)增强聚丙烯(PP)层合片材复合聚对苯二甲酸乙二酯(PET)泡沫夹芯板材,为了提高泡沫夹芯板材的基本力学性能及其尺寸的稳定性,将模压成型过程分为预热、模压两阶段,分别对应材料预热温度、保温时间、模压压力、保压时间四个工艺参数,运用正交实验方法,分析和讨论了四种工艺参数对连续GF增强PP复合PET泡沫夹芯板材厚度和弯曲强度的影响,并对各工艺参数进行了优化。结果表明,优化后的工艺参数组合为预热温度190℃、保温时间60 s、模压压力0.3 MPa、保压时间180 s,保温时间和保压时间对厚度和弯曲强度的影响程度较大。 
Abstract:Continuous glass fiber (GF) reinforced polypropylene (PP) laminated sheet composite polyethylene terephthalate (PET) foam sandwich panel was prepared by compression molding process. In order to improve the basic mechanical properties and dimensional stability of the foam sandwich panel, the molding process was divided into two stages: pre-heating process and molding process including four process parameters, corresponding to pre-heating temperature, heat holding time, molding pressure and pressure holding time. The effects of the four parameters on the thickness and bending strength of the continuous GF reinforced PP composite PET foam sandwich panel were discussed and analyzed with the orthogonal test method, and the better combination of the four process parameters was optimized. The results show that the optimized process parameters are pre-heating temperature 190℃, heat holding time 60 s, molding pressure 0.3 MPa, pressure holding time 180 s, the influences of the heat holding time and the pressure holding time on the thickness and bending strength are greater. 
关键词:连续玻纤增强聚丙烯;层合片材;聚对苯二甲酸乙二酯泡沫板;模压成型;物理力学性能 
Keywords:continuous glass fiber reinforced polypropylene; laminated sheet; polyethylene terephthalate foam panel; compression molding process; physical and mechanical properties 
本文引用格式:
袁杰,李丽,徐光磊,等.连续玻纤增强PP复合PET泡沫夹芯板的模压成型工艺[J].工程塑料应用,2019,47(12):61-65.
Yuan Jie,Li Li,Xu Guanglei,et al. Compression molding process for continuous glass fiber reinforced PP composite PET foam sandwich panel[J]. Engineering Plastics Application,2019,47(12):61-65. 

原文:
 
相似文章:
  碳纤维增强塑料机载机箱模压成型装置的设计
2019年第07期
  塑料光学透镜模压成型有限元分析
2018年第09期
  细长变截面复合材料构件模压成型工艺设计
2018年第06期
  PLA/木薯厌氧渣复合材料的制备工艺
2016年第11期
  三种植物纤维填充聚乳酸复合材料性能对比
2016年第11期
  成型方法对PE-UHMW摩擦磨损性能的影响
2016年第02期
  LGFRPP轿车底护板模压成型工艺研究
2015年第08期
  GF增强PP/苎麻纤维复合材料的制备及其性能研究
2015年第07期
  连续GF增强PP层合片材破坏形式及层间剪切强度研究
2014年第11期
  高分子材料在汽车座椅上的应用
2013年第01期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5