《工程塑料应用》 2020年第02期
DOI:10.3969/j.issn.1001-3539.2020.02.023
建筑用膨胀石墨阻燃聚氨酯泡沫材料的制备及性能
费月英
甘肃交通职业技术学院,兰州 730070 
Preparation and Properties of Flame-Retardant Polyurethane Foam with Expanded Graphite for Construction
Fei Yueying
Department of Road and Bridge Engineering of Gansu Vocational and Technical College of Communications, Lanzhou 730070, China 
摘要:在聚氨酯泡沫塑料基体中添加了不同含量的可膨胀石墨,利用其膨胀阻燃作用,制备出了一系列阻燃性能、力学性能和导热性能不同的聚氨酯泡沫塑料。结果表明,当聚氨酯泡沫塑料中添加了20质量份的可膨胀石墨时,相应聚氨酯泡沫塑料的综合性能最为理想:极限氧指数为30.1%,热释放速率峰值为98 kW/m2,火灾指数和火灾蔓延指数分别为0.420和1.273,初始热分解温度和质量保持率分别为362℃和29.8%,压缩强度为0.18 MPa,密度为49.0 kg/m3,热导率为0.027 W/(m·K)。 
Abstract:Different content of expandable graphite was added to the polyurethane foam matrix, and a series of polyurethane foam plastics with different flame retardancy, mechanical properties and thermal conductivity were prepared by using intumescent flame retardant. The experimental results show that when the polyurethane foam plastics are added 20phr of expandable graphite, the comprehensive properties of the corresponding polyurethane foam are the most ideal: The limiting oxygen index is 30.1%, the heat release rate is 98 kW/m2, the fire index and the fire spread index are 0.420 and 1.273, the initial thermal decomposition temperature and quality retention are 362℃ and 29.8%, respectively, and the compressive strength is 0.18 MPa. The density is 49.0 kg/m3, and the thermal conductivity is 0.027 W/(m·K). 
关键词:聚氨酯;可膨胀石墨;阻燃性能;力学性能;导热性能 
Keywords:polyurethane; expandable graphite; flame retardant; mechanical property; thermal conductivity 
本文引用格式:
费月英.建筑用膨胀石墨阻燃聚氨酯泡沫材料的制备及性能[J].工程塑料应用,2020,48(2):119-122.
Fei Yueying. Preparation and properties of flame-retardant polyurethane foam with expanded graphitefor construction[J]. Engineering Plastics Application,2020,48(2):119-122. 

原文:
 
相似文章:
  基于喷动床技术的超临界CO2聚氨酯珠粒发泡工艺
2020年第05期
  二胺结构对聚亚胺vitrimer材料性能的影响
2020年第05期
  导热环氧树脂复合材料研究进展
2020年第04期
  聚氨酯/无机填料复合材料制备及性能
2020年第04期
  TPU/EVAC共混发泡材料制备及性能
2020年第04期
  热膨胀微球发泡剂对TPU泡沫结构与性能影响
2020年第04期
  丙烯基弹性体和乙烯-辛烯共聚物增韧聚丙烯性能
2020年第04期
  PE-HD/GNP/MWCNT纳米复合材料性能
2020年第04期
  MWCNT分布对POE/PA12复合材料性能影响
2020年第03期
  注塑工艺对玻纤增强PBT/微球发泡材料力学性能的影响
2020年第02期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5