《工程塑料应用》 2020年第05期
DOI:10.3969/j.issn.1001-3539.2020.05.009
再生PVDF/蒙脱土纳米复合材料制备与性能
谭寿再,孙永红,林嘉定,卢恩尧
广东轻工职业技术学院,广东省高分子材料先进加工工程研究中心,广州 510300 
Preparation and Properties of Recycled PVDF/MMT Nanocomposites
Tan Shouzai, Sun Yonghong, Lin Jiading, Lu Enyao
Advanced Research Center for Polymer Processing Engineering of Guangdong Province, Guangdong Industry Polytechnic, Guangzhou 510300, China 
摘要:通过新型非对称双螺杆挤出机制备再生聚偏氟乙烯(PVDF)/蒙脱土(MMT)纳米复合材料,采用傅里叶变换红外光谱仪、差示扫描量热仪、热重分析仪、扫描电子显微镜(SEM)、转矩流变仪和万能电子试验机等对材料进行表征测试,研究MMT含量对复合材料结构和性能的影响。结果表明,MMT对复合材料的结晶行为有一定的影响,添加MMT后复合材料的熔融温度、结晶温度和结晶度都有提高,添加1% MMT复合材料的熔融温度和结晶温度分别比未加MMT的再生PVDF提高1℃和0.94℃;再生PVDF/MMT复合材料的降解温度随着MMT含量增加而降低,失重50%的温度反而随MMT含量增加而升高;SEM发现,MMT以100~200 nm的片状分散在PVDF基体中,随着MMT含量增加,出现MMT团聚、脱落现象;在实验范围内,随着MMT含量的增加,复合材料的拉伸强度和缺口冲击强度随之提高,添加5% MMT复合材料的拉伸强度比未添加MMT的提高33.5%,缺口冲击强度提高29.7%;转矩流变实验发现,适量的MMT增加了复合材料加工时的剪切作用,降低了熔体塑化平衡扭矩。 
Abstract:In order to study the effects of montmorillonite (MMT) contents on the structure and properties of recycled polyvinylidene fluoride (PVDF)/MMT nanocomposites, FTIR, DSC, TGA, SEM, torque rheometer and universal electronic tester were used to conduct characterization test on the samples of the composites, which were made from a new type of asymmetric twin-screw extruder. The results show that, MMT can affect the crystallization behavior of the composites, adding MMT results in the increase of melting temperature, crystallization temperature and crystallinity, the melting temperature and crystallization temperature of the composite with 1 wt% MMT are 1℃ and 0.94℃ higher than the PVDF recycled materials without MMT, respectively. The degradation temperature of recycled PVDF/MMT composites decreases with the increase of MMT content, and the temperature of 50% weight-loss increases with the increase of MMT content. Also, SEM finds that MMT is distributed in PVDF matrix in sheets of 100-200 nm, with the increase of MMT, MMT becomes aggregated and shredded. Within the experimental range, as MMT content increases, the tensile strength and notched impact strength of the composites increase, the tensile strength of the composite with 5 wt% MMT is increased by 33.5% and the notched impact strength is increased by 29.7% compared with the non-added MMT. The results of torque rheological experiments show that, the MMT nano-particles with appropriate amount can increase the processing shear effect of the composites and reduce the melt plasticizing equilibrium torque. 
关键词:聚偏氟乙烯;蒙脱土;复合材料;再生;性能 
Keywords:polyvinylidene fluoride; montmorillonite; composite; recycle; property 
基金:广东省科技计划项目(2016A010103046),广东高校工程中心建设滚动项目(2013 CXZDB004) 
本文引用格式:
谭寿再,孙永红,林嘉定,等.再生PVDF/蒙脱土纳米复合材料制备与性能[J].工程塑料应用,2020,48(5):46-51.
Tan Shouzai,Sun Yonghong,Lin Jiading,et al. Preparation and properties of recycled PVDF/MMT nanocomposites[J]. Engineering Plastics Application,2020,48(5):46-51. 

原文:
 
相似文章:
  碳纳米管含量对聚酰亚胺/碳纤维复合材料性能的影响
2020年第05期
  碳纳米管改性环氧树脂/碳纤维复合材料的界面性能
2020年第05期
  热处理温度对苎麻纤维增强酚醛树脂复合材料性能影响
2020年第05期
  PLA增强改性PBS共混物制备及性能
2020年第05期
  PA66-气凝胶复合粉体制备及性能
2020年第05期
  衬底对聚偏氟乙烯-三氟乙烯基纳米能量发生器压电性能的影响
2020年第05期
  空心玻璃微珠对聚丙烯酸水凝胶溶胀性能的影响
2020年第05期
  二胺结构对聚亚胺vitrimer材料性能的影响
2020年第05期
  真空辅助树脂传递模塑成型工艺研究进展
2020年第04期
  填充型导电高分子基气敏纳米复合材料研究进展
2020年第04期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5