低吸水率和低介电损耗PTFE/SiO2复合材料制备
金霞,张立欣,鲁思如,贾倩倩,冯春明
中国电子科技集团公司第四十六研究所,天津 300220 
Preparation of Low Water Absorption and Dielectric Loss PTFE/SiO2 Composites
Jin Xia, Zhang Lixin, Lu Siru, Jia Qianqian, Feng Chunming
The 46th Research Institute of China Electronics Technology Group Corporation, Tianjin 300220, China 
摘要:研究了SiO2的改性以及改性SiO2对PTFE/SiO2复合材料介电和吸水性能的影响。结果证明,SiO2经改性后,PTFE/SiO2复合材料的吸水率和介电损耗明显降低,傅立叶变换红外光谱和X光电子能谱显示经偶联剂改性处理后,硅烷偶联剂包覆在SiO2表面,改善了其与树脂基体之间界面性能,进而对复合材料的各项性能产生影响。扫描电子显微镜观察,复合材料界面间结合紧密。硅烷偶联剂改性SiO2过程中加入适量的乙酸,可以使改性效果更佳,制备的PTFE/SiO2复合材料各项性能最佳,介电常数达到2.933,损耗因子降至0.0013,复合材料热压烧结后的密度达到2.116 g/cm 3、吸水率降至0.035%,热膨胀系数降至36×10-6 K-1。  
Abstract:The modification of SiO2 and its influence on the dielectric and water absorption properties of PTFE/SiO2 composites were studied. The results show that the dielectric and water absorption properties of PTFE/SiO2 composites are significantly reduced after the modification of SiO2. In addition, according to the results of FTIR and EDS, SiO2 is effectively coated with silane coupling agents, which affectes the properties of the composites. The SEM of PTFE/SiO2 composites indicates that the interfacial binding force between SiO2 and PTFE is obviously increased. The performance of the composites prepared by the SiO2 treated by alcoholic solution of acetic acid are optimized. The permittivity, dielectric loss, the density after hot pressing, water absorption and coefficient of thermal expansion are reached to 2.933, 0.0013, 2.116 g/cm3, 0.035% and 36×10-6K-1 , respectively.  
关键词:水解溶剂;偶联剂;聚四氟乙烯;二氧化硅;介电性能;密度;吸水率;热膨胀系数 
Keywords:hydrolysis solvents; coupling agents; PTFE; SiO2; dielectric properties; density; water absorption; coefficient of thermal expansion 
本文引用格式:
金霞,张立欣,鲁思如,等.低吸水率和低介电损耗PTFE/SiO2复合材料制备[J].工程塑料应用,2020,48(7):33-37.
Jin Xia,Zhang Lixin,Lu Siru,et al. Preparation of low water absorption and dielectric loss PTFE/SiO2 composites[J]. Engineering Plastics Application,2020,48(7):33-37. 

原文:
论文未上传  
相似文章:
  PTFE中空纤维微孔膜制备工艺及应用研究进展
2020年第07期
  成型方法对PE-UHMW/PE-HD共混物流变行为和力学性能影响
2020年第07期
  插层水滑石的抑烟性能研究
2020年第06期
  不同固体润滑填料对聚四氟乙烯性能的影响
2020年第06期
  良外观耐高静压玻纤增强PA66复合材料制备及性能
2020年第06期
  聚氨酯/无机填料复合材料制备及性能
2020年第04期
  挤出工艺对纳米碳酸钙母料性能影响
2020年第04期
  PE-HD/GNP/MWCNT纳米复合材料性能
2020年第04期
  PP/PA6/SiO2纳米复合材料的非等温结晶动力学
2020年第03期
  紫外吸收剂DPP对PE-LD棚膜性能的影响
2020年第02期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5