玻璃纤维/甲基丙烯酸改性环氧树脂复合材料制备
马开宝,高守臻,李大勇,王晓立,罗长宏,魏化震,郑志才,于广
山东非金属材料研究所,济南 250031 
Preparation and Properties of Glass Fiber/Methacrylic Acid Modified Epoxy Resin Composites
Ma Kaibao, Gao Shouzhen, Li Dayong, Wang Xiaoli, Luo Changhong, Wei Huazhen, Zheng Zhicai, Yu Guang
Shandong Institute of Non-metallic Materials, Jinan 250031, China 
摘要:通过甲基丙烯酸(MAA)与环氧基团之间的反应得到MAA接枝改性的环氧树脂,然后采用真空灌注工艺制备了玻璃纤维/MAA改性环氧树脂复合材料,研究了反应时间、催化剂用量对MAA接枝率的影响以及MAA接枝率、苯乙烯含量、纤维含量对复合材料性能的影响。结果表明,反应时间5 h后MAA接枝率达到最大值;催化剂用量为环氧树脂质量的0.35%时MAA接枝率最高且反应平稳;MAA接枝率越高复合材料的力学性能越高;苯乙烯含量为15%时,复合材料的拉伸强度达到最大值,苯乙烯的含量为10%时,复合材料的弯曲强度、层间剪切强度达到最大值;纤维含量为60%时复合材料的力学性能最佳。  
Abstract:The methacrylic acid (MAA) graft modified epoxy resin was obtained by the reaction between MAA and epoxy groups. Then the glass fiber/MAA modified epoxy resin composite was prepared by vacuum infusion process. The reaction time was studied. The effect of catalyst dosage on the grafting rate of MAA and the effect of MAA grafting rate, styrene content and fiber content on the properties of composites was studied. The results show that the grafting rate of MAA reaches the maximum after 5 h reaction time; the grafting rate of MAA is the highest and the reaction is stable when the amount of catalyst is 0.35% of epoxy resin resin; the higher the grafting rate of MAA, the higher the mechanical properties of the composite is. When the styrene content is 15%, the tensile strength of the composite reaches the maximum value, the flexural strength and interlaminar shear strength of the composite reach the maximum when the content of styrene is 10%, the mechanical properties of the composite are best when the fiber content is 60%. 
关键词:甲基丙烯酸;环氧树脂;玻璃纤维;接枝改性;复合材料 
Keywords:methacrylic acid; epoxy resin; glass fiber; graft modification; composite 
本文引用格式:
马开宝,高守臻,李大勇,等.玻璃纤维/甲基丙烯酸改性环氧树脂复合材料制备[J].工程塑料应用,2020,48(7):44-49.
Ma Kaibao,Gao Shouzhen,Li Dayong,et al. Preparation and properties of glass fiber/methacrylic acid modified epoxy resin composites[J]. Engineering Plastics Application,2020,48(7):44-49. 

原文:
论文未上传  
相似文章:
  复合材料传动轴的应用及技术研究进展
2020年第07期
  DOPO和含磷固化剂协同阻燃EP性能
2020年第07期
  苎麻织物铺层设计及化学改性对复合材料力学及界面性能影响
2020年第07期
  ABS/PBT合金材料制备与性能
2020年第07期
  连续玻纤增强PA6复合材料的制备
2020年第07期
  聚氨酯/铕复合材料制备及发光性能
2020年第07期
  低温等离子体处理芳纶复合材料界面性能研究进展
2020年第06期
  纤维增强复合材料薄壁件轴向压缩吸能性研究进展
2020年第06期
  基于聚维酮碘改性的抗菌复合材料的研究进展
2020年第06期
  冲击能量对EW200/E51复合材料层合板损伤的影响
2020年第06期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5