压装炸药防护层制备工艺的优化及其性能
蒲虹蓉1,罗观2,吴奎先2,刘绪望2,唐长兴2,赵天波1
1.北京理工大学化学与化工学院,北京 100081; 2.中国工程物理研究院化工材料研究所,四川绵阳 621900 
Optimization of Preparation Process and Performance of Protective Layer for Pressurized Explosive
Pu Hongrong1, Luo Guan2, Wu Kuixian2, Liu Xuwang2, Tang Changxing2 , Zhao Tianbo1
1. School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, China; 2. Institute of Chemical Materials, China Institute of Engineering Physics, Mianyang 621900, China 
摘要:在压装炸药表面增加保护涂层,可以提高压装炸药的安全稳定性。探索用石蜡聚集体、热熔性高强度氟碳树脂、聚氨酯、聚酰亚胺及其合金材料制备压装炸药防护层。通过对热压融合过程不同配方材料的成型观察、防护层的硬度以及防护层与药柱的粘结性的测试,制备出了符合热压融合工艺的防护层材料,其中热塑性聚氨酯90(粉末)+ SiO2,PI+铝粉样品性能优异,达到防护层生产工艺能一次性成型,简便快速的要求。  
Abstract:Adding a protective coating on the surface of the pressed explosive can improve the safety and stability of the pressed explosive. A new type of paraffin aggregate is used as the basic protective layer for this project, and the protective layer material for press-fit explosives is developed, including fluorocarbon resin, polyurethane, polyimide and their alloy materials. Through the observation of the forming of different formula materials, the hardness of the protective layer and the testing of the adhesion between the protective layer and the grain during the hot-pressing fusion process, the protective layer materials conforming to the hot-pressing fusion process are prepared, among which thermoplasticity polyurethane90 (powder)+SiO2, PI + aluminum powder samples have excellent performance and meet the requirements of one-time forming and simplicity and rapidness in the production process of the protective layer.  
关键词:压装炸药;防护层材料;石蜡聚集体;氟碳树脂;聚氨酯;聚酰亚胺 
Keywords:pressed explosives; protective layer materials; paraffin aggregates; fluorocarbon resin; polyurethane; polyimide 
基金:国家自然科学基金项目(20973022,11472048) 
本文引用格式:
蒲虹蓉,罗观,吴奎先,等.压装炸药防护层制备工艺的优化及其性能[J].工程塑料应用,2020,48(7):50-55.
Pu Hongrong,Luo Guan,Wu Kuixian,et al. Optimization of preparation process and performance of protective layer for pressurized explosive[J]. Engineering Plastics Application,2020,48(7):50-55. 

原文:
论文未上传  
相似文章:
  聚氨酯/铕复合材料制备及发光性能
2020年第07期
  热处理温度对碳纤维增强聚酰亚胺复合材料性能影响
2020年第06期
  聚酰亚胺改性耐高温透波邻苯二甲腈复合材料制备
2020年第06期
  碳纳米管含量对聚酰亚胺/碳纤维复合材料性能的影响
2020年第05期
  基于喷动床技术的超临界CO2聚氨酯珠粒发泡工艺
2020年第05期
  TPU/EVAC共混发泡材料制备及性能
2020年第04期
  热膨胀微球发泡剂对TPU泡沫结构与性能影响
2020年第04期
  建筑用膨胀石墨阻燃聚氨酯泡沫材料的制备及性能
2020年第02期
  建筑用阻燃聚氨酯研究进展
2020年第01期
  APP/BF-KH550协同阻燃热塑性聚氨酯的性能
2020年第01期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5