冷却系统对ABS材质汽车后视镜外壳翘曲变形影响
赵天德
梧州职业学院,广西梧州 543002 
Influence of Cooling System on Warpage and Deformation of ABS Automotive Rearview Mirror Shell
Zhao Tiande
Wuzhou Vocational College, Wuzhou 543002, China 
摘要:首先对丙烯腈-丁二烯-苯乙烯塑料(ABS)材质的汽车后视镜外壳的注塑加工工艺进行了优化,最终确定了其工艺为:料筒温度、注塑压力、保压压力、保压时间、模具温度分别为260℃,11 MPa,2 MPa,5.0 s,60℃。通过Moldflow软件对ABS材质的汽车后视镜外壳模具冷却系统进行了仿真模拟,并确定了最佳的冷却方案:冷却管路直径为10 mm,管路数目为1根,排列方式处于模具单侧排列,冷却液温度为20℃。仿真结果表明,冷却管路进口和出口的冷却液温度分别为20.02 ℃和25.20℃;总体冷却时间为30.37 s;注塑件底面最高温度为60.21℃;Z方向的最大翘曲变形量为1.031 mm。另外,还以实际注塑实验对模拟结果进行了验证,10次注塑的结果均与模拟结果十分接近,标准差仅为0.003 mm。  
Abstract:The injection molding process of ABS automotive rearview mirror shell was optimized, and the process was determined as follows: barrel temperature, injection pressure, holding pressure, holding time and mould temperature are 260℃, 11 MPa, 2 MPa, 5.0 s and 60℃respectively. In addition, the mold cooling system of automobile rearview mirror shell made of ABS material was simulated by Moldflow software, and the optimal cooling scheme is determined: the diameter of cooling pipeline is 10 mm, the number of pipeline is 1, the arrangement mode is arranged on one side of the mold, and the temperature of coolant is 20℃. The simulation results show that the coolant temperature at the inlet and outlet of the cooling pipe is 20.02℃and 25.20℃respectively, the total cooling time is 30.37 s; the maximum ground temperature of the injection molding part is 60.21℃, the maximum warpage deformation in the Z direction is 1.031 mm. In addition, the simulation results are verified by the actual injection experiments. The results of 10 injection molding are very close to the simulation results, and the standard deviation is only 0.003 mm. 
关键词:汽车后视镜外壳;注塑工艺;模拟仿真;翘曲变形 
Keywords:automotive rearview mirror shell; injection molding process; simulation; warpage 
本文引用格式:
赵天德.冷却系统对ABS材质汽车后视镜外壳翘曲变形影响[J].工程塑料应用,2020,48(7):75-79.
Zhao Tiande. Influence of cooling system on warpage and deformation of ABS automotive rearview mirror shell[J]. Engineering Plastics Application,2020,48(7):75-79. 

原文:
论文未上传  
相似文章:
  注塑工艺对GFPP/可膨胀微球发泡制件收缩率的影响
2020年第05期
  注塑工艺对玻纤增强PBT/微球发泡材料力学性能的影响
2020年第02期
  注塑机料筒温度调控和计算机仿真研究
2020年第01期
  基于预变形的汽车碳罐盖板翘曲变形优化
2019年第10期
  基于Moldex3D和灰色关联理论在空气滤清器上壳的工艺优化
2018年第10期
  化学发泡注塑工艺对PA6/GF微发泡材料结构与力学性能的影响
2018年第09期
  基于Moldflow的PUR车轮注塑工艺参数优化
2018年第06期
  基于CAE技术的翘曲分析及反变形补偿设计
2018年第05期
  注塑工艺对哑光PC/ABS冲击性能的影响
2018年第05期
  基于BP神经网络和遗传算法的机箱壳注塑工艺参数多目标优化
2018年第03期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5