《工程塑料应用》 2020年第09期
DOI:10.3969/j.issn.1001-3539.2020.09.003
球磨时间对环氧树脂/FeSiCr复合材料电磁性能及吸波性能影响
翟影12,朱冬梅1,罗发1,南涵漪1,阮兴翠2
1.西北工业大学国家凝固技术国家重点实验室,西安 710072; 2.陕西华秦科技实业有限公司,西安 710076 
Effects of Milling Time on Electromagnetic and Microwave Absorbing Properties of Epoxy Resin/FeSiCr Composites
Zhai Ying12, Zhu Dongmei1, Luo Fa1, Nan Hanyi1, Ruan Xingcui2
1. State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China; 2. Shaanxi Huaqin Technology Industry Ltd., Xi'an 710072, China) 
摘要:采用高能机械球磨法制备片状FeSiCr合金吸收剂,利用X射线衍射仪、扫描电子显微镜和矢量网络分析仪分析研究球磨时间对FeSiCr合金相结构、微观形貌及环氧树脂/FeSiCr复合材料电磁性能及吸波性能的影响。研究结果表明,随着球磨时间延长,FeSiCr合金由球状变为片状,环氧树脂/FeSiCr复合材料的复介电常数和复磁导率逐渐增大。球磨时间达5 h时,获得厚片状FeSiCr合金,制备的复合材料试样厚度为1.4 mm时,在6.6~18 GHz波段反射率小于-5 dB,吸波性能优异。球磨时间延长至8 h和11 h时,获得薄片状FeSiCr合金,制备的复合材料试样厚度为2 mm时,在低频波段具有优异的吸波性能,分别在3.5 GHz和2.97 GHz达到反射率峰值-8.03 dB和-9.28 dB。通过调整球磨时间,可使环氧树脂/FeSiCr复合材料在2.6~18 GHz内不同频段实现优异的吸波性能。 
Abstract:Flaky FeSiCr alloy absorbent was fabricated by mechanical milling method. The effects of milling time on phase, morphology of FeSiCr alloy, electromagnetic and microwave absorbing properties of epoxy resin/FeSiCr composites were characterized by X-ray diffractometer, scanning electron microscopy and vector network analyzer. The results show that the microscopy of the FeSiCr alloy particles are changed from sphere to flaky shape, and the complex permittivity and complex permeability of epoxy resin/FeSiCr composites are increased with milling time increases. Thick flaky FeSiCr alloy is achieved after milled with 5 h, and the reflection loss (RL) below -5 dB of epoxy resin/FeSiCr composite is obtained in the high frequency range of 6.6-18 GHz at the thickness of 1.4 mm, demonstrating a good microwave absorption performance. When the milling time is extended to 8 h and 11 h, thin flaky FeSiCr alloy is reached, and the RL peak values are -8.03 dB at 3.5 GHz and -9.28 dB at 2.97 GHz for epoxy resin/FeSiCr composite at the thickness of 2.0 mm, respectively. The outstanding microwave absorbing property of epoxy resin/FeSiCr composites in the different frequency bands in 2.6-18 GHz can be fulfilled by adjustment of milling time of FeSiCr alloy. 
关键词:环氧树脂/FeSiCr复合材料;球磨时间;介电常数;磁导率;吸波性能 
Keywords:epoxy resin/FeSiCr composite; milling time; permittivity; permeability; microwave absorbing property 
基金:国家自然科学基金项目(51402239) 
本文引用格式:
翟影,朱冬梅,罗发,等.球磨时间对环氧树脂/FeSiCr复合材料电磁性能及吸波性能影响[J].工程塑料应用,2020,48(9):13-18.
Zhai Ying,Zhu Dongmei,Luo Fa,et al. Effects of milling time on electromagnetic and microwave absorbing properties of epoxy resin/FeSiCr composites[J]. Engineering Plastics Application,2020,48(9):13-18. 

原文:
 
相似文章:
  多孔结构聚酰亚胺基介电材料研究进展
2020年第10期
  不同无机物改性热致液晶聚合物材料的介电性能
2019年第07期
  SiC改性氰酸酯树脂/三甲氧基乙烯基硅烷材料的制备
2018年第10期
  短切导电纤维结构复合材料吸波性能研究
2015年第08期
  铁氧体复合材料吸波性能研究进展
2015年第07期
  低介电常数聚酰亚胺材料制备方法研究进展
2015年第05期
  氰酸酯/G-POSS杂化材料的制备及性能研究
2014年第05期
  树脂含量对环氧树脂基覆铜板性能的影响
2014年第03期
  新型功能性聚酰亚胺的研究与应用进展
2013年第01期
  聚醚酰亚胺对炭黑填充环氧树脂复合材料导电性能和吸波性能的影响
2012年第07期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5