《工程塑料应用》 2020年第09期
DOI:10.3969/j.issn.1001-3539.2020.09.009
工艺参数对聚苯醚包覆环氧树脂微胶囊结构与性能影响
刘姝辰,胡义,李楠,袁莉,顾嫒娟,梁国正
苏州大学材料与化学化工学部,江苏苏州 215123 
Effects of Process Parameters on Structure and Properties of Polyphenylene Ether Microcapsules Filled with Epoxy Resin
Liu Shuchen, Hu Yi, Li Nan, Yuan Li, Gu Aijuan, Liang Guozheng
College of Chemistry, Chemical Engineering and Materials Science, Soochow University, Suzhou 215123, China 
摘要:为了研究溶剂挥发法制备高热稳定性、低分子量聚苯醚(PPE)包覆环氧树脂(EP)微胶囊(MCs)过程中工艺参数对MCs结构与性能的影响,通过改变工艺参数PPE/EP质量比、表面活性剂十二烷基硫酸钠(SDS)浓度以及搅拌速率制备了MCs。结果表明,采用溶剂挥发法制备的MCs的平均粒径范围为9.8~32 μm。PPE/EP质量比、SDS浓度及搅拌速率可明显影响MCs的结构与性能。增加PPE/EP的质量比、SDS浓度和搅拌速率有利于小粒径及低孔隙结构MCs的形成,形成的小粒径MCs具有相对高的化学反应活性及低的初始热分解温度,但其具有相对高的最大热分解温度。当PPE与EP质量比为1∶1,SDS浓度为0.25%及搅拌速率为700 r/min时,所制备的MCs的结构与热稳定性相对较好。 
Abstract:To investigate the influences of process parameters on the structure and properties of high thermal stability and low molecular weight polyphenylene ether (PPE) microcapsules (MCs) filled with epoxy resin (EP) prepared by the solvent evaporation method, MCs were prepared by varying process parameters including the mass ratios of PPE/EP, surfactant sodium dodecyl sulphate (SDS) concentration and agitation rate. Results indicate that the average particle size of MCs prepared by the solvent evaporation method is 9.8-32 μm. The structure and properties of MCs depend strongly on the mass ratio of PPE/EP, the concentration of SDS and the agitation rate. Increasing the mass ratio of PPE/EP, SDS concentration and agitation rate facilitate the formation of smaller MCs with low pore structure. The smaller MCs have relatively high chemical reaction activity and low initial thermal decomposition temperature, but they show higher maximum thermal decomposition temperature. MCs with better structure and thermal stability can be obtained when the mass ratio of PPE/EP is 1/1, SDS concentration is 0.25% and agitation rate is 700 r/min. 
关键词:微胶囊;聚苯醚;环氧树脂;形貌;热性能 
Keywords:microcapsule; polyphenylene ether; epoxy resin; morphology; thermal property 
基金:国家自然科学基金面上项目(51973145),江苏省高校优势学科建设工程项目(PAPD),苏州大学大学生创新创业训练项目(2013xj021) 
本文引用格式:
刘姝辰,胡义,李楠,等.工艺参数对聚苯醚包覆环氧树脂微胶囊结构与性能影响[J].工程塑料应用,2020,48(9):49-55.
Liu Shuchen,Hu Yi,Li Nan,et al. Effects of process parameters on structure and properties of polyphenylene ether microcapsules filled with epoxy resin[J]. Engineering Plastics Application,2020,48(9):49-55. 

原文:
 
相似文章:
  加速老化对PLA/TiO2复合材料性能影响
2020年第09期
  生物质腰果酚基环氧树脂体系固化工艺及性能
2020年第09期
  环氧树脂/空心玻璃微珠复合浮力材料制备及性能
2020年第09期
  EP/GF/DiDOPO复合材料阻燃性能
2020年第09期
  氰酸酯树脂/纳米立方氮化硼复合材料制备及性能
2020年第09期
  球磨时间对环氧树脂/FeSiCr复合材料电磁性能及吸波性能影响
2020年第09期
  PA6/CaCO3/GNPs导热复合材料制备及性能
2020年第09期
  车用连续纤维增强热塑性环氧树脂复合材料制备及性能
2020年第08期
  含苯并噁唑结构耐高温聚酰亚胺模塑料制备及性能
2020年第08期
  DOPO和含磷固化剂协同阻燃EP性能
2020年第07期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5