《工程塑料应用》 2020年第12期
DOI:10.3969/j.issn.1001-3539.2020.12.002
静电纺丝法制备PI/MOF-808混合基质膜及性能
翟燕1,谢建新2,刘浩1,薛亚楠1,王鹏祥1,石浩楠1,王祥青1
1.太原工业学院,太原 030008; 2.中北大学,太原 030051 
Preparation and Properties of PI/MOF-808 Mixed Matrix Membrane by Electrostatic Spinning
Zhai Yan1, Xie Jianxin2, Liu Hao1, Xue Yanan1, Wang Pengxiang1, Shi Haonan1, Wang Xiangqing1
1.Taiyuan Institute of Technology, Taiyuan 030008, China; 2.North University of China, Taiyuan 030051, China 
摘要:以金属有机骨架材料(MOF-808)为填料,将其加入到均苯四甲酸二酐-4,4’-二氨基二苯醚(PMDA-ODA)型聚酰亚胺(PI)前驱体中,通过静电纺丝法制备出不同MOF-808添加量的PI混合基质膜。采用傅立叶变换红外光谱仪、X射线衍射仪、扫描电子显微镜和拉伸试验机、热重分析仪对MOF-808晶体结构和PI/MOF-808混合基质膜的形貌、力学性能、孔隙率、吸液率及热稳定性进行表征。结果表明,在PI中添加MOF-808,PI/MOF-808混合基质膜有序度和交联程度增大,拉伸强度和热稳定性随晶体添加量的增加而增大,MOF-808质量分数为0.5%的混合基质膜的拉伸强度是纯PI纤维膜的1.5倍;孔隙率和吸液率随着MOF-808添加量的增加而降低,MOF-808质量分数为0.7%的混合基质膜的孔隙率和吸液率是常用聚烯烃隔膜的1.6倍和7.4倍。 
Abstract:Adding metal organic framework material (MOF-808) into precursor of pyromellitic dianhydride and 4,4' -oxydianiline (PMDA-ODA) polyimide (PI) precursor, PI mixed matrix membrane with different amount of MOF-808 were prepared by electrospinning. The morphology, mechanical properties, porosity and liquid absorption and thermal stability of PI/MOF-808 mixed matrix membrane were characterized by Fourier transform infrared spectroscopy (FTIR), X ray diffraction (XRD), scanning electron microscope (SEM), tensile testing machine and thermogravimetric analyzer. The results show that the ordering degree and crosslinking degree of PI/MOF-808 mixed matrix membrane increase after MOF-808 is added into PI. The tensile strength and thermal stability of PI/MOF-808 mixed matrix membrane increase with the increase of crystal addition. When the addition amount of MOF-808 is 0.5%, the tensile strength of mixed matrix membrane is 1.5 times that of pure PI fiber membrane. Porosity and liquid absorption decrease with the increase of MOF-808 crystal addition. When the addition amount of MOF-808 is 0.7%, the porosity of PI is 1.6 times that of polyolefin diaphragm, and the liquid absorption rate is 7.4 times that of polyolefin diaphragm. 
关键词:MOF-808;聚酰亚胺;静电纺丝;混合基质膜 
Keywords:MOF-808; polyimide; electrostatic spinning; mixed matrix membran 
基金:山西省“1331工程”协同创新中心建设计划项目 
本文引用格式:
翟燕,谢建新,刘浩,等.静电纺丝法制备PI/MOF-808混合基质膜及性能[J].工程塑料应用,2020,48(12):6-10.
Zhai Yan,Xie Jianxin,Liu Hao,et al. Preparation and properties of PI/MOF-808 mixed matrix membrane by electrostatic spinning[J]. Engineering Plastics Application,2020,48(12):6-10. 

原文:
 
相似文章:
  熔体微分电纺制备超支化PPS超细纤维
2020年第12期
  多孔结构聚酰亚胺基介电材料研究进展
2020年第10期
  多射流静电纺丝稳定性的影响分析
2020年第10期
  含苯并噁唑结构耐高温聚酰亚胺模塑料制备及性能
2020年第08期
  PVDF/类石墨相氮化碳电纺锂电池隔膜制备及性能
2020年第08期
  压装炸药防护层制备工艺的优化及其性能
2020年第07期
  静电纺PVDF/铌酸钠复合纤维膜制备及压电性能
2020年第07期
  热处理温度对碳纤维增强聚酰亚胺复合材料性能影响
2020年第06期
  聚酰亚胺改性耐高温透波邻苯二甲腈复合材料制备
2020年第06期
  碳纳米管含量对聚酰亚胺/碳纤维复合材料性能的影响
2020年第05期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878278 传真:0531-85947355
鲁ICP备05018524号-5