《工程塑料应用》 2021年第02期
DOI:10.3969/j.issn.1001-3539.2021.02.001
高热稳定性低氯聚苯砜树脂合成及表征
徐显骏12,高红军12,孙学科12,陈锐斌12,姜苏俊12,曹民12
1.金发科技股份有限公司国家认定企业技术中心,广东省特种工程塑料重点实验室,广州 510663; 2.珠海万通特种工程塑料有限公司,广东珠海 519000 
Synthesis and Characterization of Low Chlorine Poly(phenylene sulfone) Resin with High Thermostability
Xu Xianjun12, Gao Hongjun12, Sun Xueke12, Chen Ruibin12, Jiang Sujun12, Cao Min12
1. National-certified Enterprise Technology Center, Kingfa Science and Technology Co., Ltd., Guangdong Key Laboratory for Specialty Engineering Plastics, Guangzhou 510663, China; 2. Zhuhai Vanteque Specialty Engineering Plastics Co., Ltd., Zhuhai 519000, China 
摘要:结合缩聚方法和封端修饰方法合成苯酚封端的聚苯砜(PPSU)树脂,利用离子色谱方法对PPSU树脂的氯端基含量进行定量测试,并采用毛细管流变仪和高温注塑等方法对比评估了不同氯端基含量PPSU树脂的热稳定性和颜色。结果表明,通过苯酚封端,PPSU树脂的氯端基含量可由3000 mg/kg以上降至700 mg/kg以下,氯端基含量取代比例可达80.6%,同时PPSU树脂的力学性能未发生明显变化,拉伸强度、屈服点伸长率、弯曲强度和缺口冲击强度分别保持在73 MPa,89%,114 MPa和50 kJ/m2左右,并且PPSU树脂的热稳定性得到一定程度提高,颜色等级有所改善。 
Abstract:Poly(phenylene sulfone) (PPSU) resins with phenol sealing end were synthesized through polycondensation reaction and terminal chemical modification method. And the chlorine end group content of resultant resins were characterized by ion chromatography. The capillary rheological test and high temperature molding methods were performed to assess the thermostability and color of the resins with different chlorine end group content. The results indicate that the chlorine end group content of the resins can be reduced from more than 3000 mg/kg to lower than 700 mg/kg, and the content of chlorine end group can be substituted up to 80.6%. At the same time, the mechanical properties including tensile strength, elongation at yield point, flexural strength and notched impact strength were not changed obviously and maintained at about 73 MPa, 89%, 114 MPa and 50 kJ/m2 respectively. Meanwhile, the thermal stability and the color grade have improved to some extent. 
关键词:聚苯砜;低氯含量;端基修饰;热稳定性;合成 
Keywords:poly(phenylene sulfone); low chlorine content; terminal chemical modification; thermostability; synthesis 
基金:广州市科技计划项目(201806010042) 
本文引用格式:
徐显骏,高红军,孙学科,等.高热稳定性低氯聚苯砜树脂合成及表征[J].工程塑料应用,2021,49(2):1-6.
Xu Xianjun,Gao Hongjun,Sun Xueke,et al. Synthesis and characterization of low chlorine poly(phenylene sulfone) resin with high thermostability[J]. Engineering Plastics Application,2021,49(2):1-6. 

原文:
 
相似文章:
  生物基共聚酯PBSeT制备与性能
2021年第02期
  不同酸根离子制备MgO/TiO2对PVC膜性能的影响
2021年第01期
  无卤阻燃永久抗静电GFPP材料研制
2021年第01期
  半芳香族耐高温尼龙PA6T/6I基LDS功能材料制备及性能
2021年第01期
  超支化聚合离子液体的应用研究进展
2020年第12期
  抗氧剂对聚亚苯基砜热稳定性影响
2020年第12期
  具有抗氧功能封端剂对耐高温PA6T/66性能影响
2020年第11期
  哌嗪磷酸盐类阻燃剂合成及应用研究进展
2020年第09期
  湿热-高温循环老化对环氧乙烯基酯树脂/玻璃纤维复合材料性能影响
2020年第09期
  热处理温度对苎麻纤维增强酚醛树脂复合材料性能影响
2020年第05期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878148 85878278
鲁ICP备05018524号-5