《工程塑料应用》 2021年第08期
DOI:10.3969/j.issn.1001-3539.2021.08.004
苯基次磷酸锌与MCA协效阻燃PLA的性能
张咪1,丁晓庆2,王克智1,王新龙2
1.山西省化工研究所(有限公司),太原 030006; 2.南京理工大学,南京 210094 
Performance of Synergistic Flame Retardant PLA with Zinc Phenyl Hypophosphite and MCA
Zhang Mi1, Ding Xiaoqing2, Wang Kezhi1, Wang Xinlong2
1. Shanxi Chemical Research Institute Co., Ltd., Taiyuan 030006, China; 2. Nanjing University of Science & Technology, Nanjing 210094, China 
摘要:利用多元素协同阻燃的理念,将自制的苯基次磷酸锌(BPA-Zn)与氰脲酸三聚氰胺(MCA)复配得到BPA-Zn/MCA复合阻燃体系,然后利用熔融共混的方式将阻燃体系与聚乳酸(PLA)基体共混得到PLA/BPA-Zn/MCA复合材料,研究了BPA-Zn/MCA阻燃体系对PLA力学、热稳定和阻燃等性能的影响。研究发现,BPA-Zn可以改善MCA与PLA基体两相间的界面相容性,而MCA起到一定的促进结晶的效果。同时,MCA与BPA-Zn之间均存在良好的协同效果,PLA复合材料阻燃性能优异。当BPA-Zn和MCA总质量分数为30%,质量比为1∶1时,复合材料极限氧指数达到28.0%,垂直燃烧阻燃等级达到V-0级,无熔滴产生。 
Abstract:The synergistic flame retardant system was prepared by compounding the self-made zinc phenyl hypophosphite (BPA-Zn) with melamine cyanurate (MCA) based on the concept of multi-element synergistic flame retardance. Polylactic acid (PLA)/BPA-Zn/MCA composites were prepared by melt-blending with BPA-Zn/MCA and PLA matrix. The effects of BPA-Zn/MCA flame retardant system on the mechanical properties, thermal stability and flame retardancy of PLA were studied. The experimental results show that BPA-Zn can improve the compatibility between MCA and PLA matrix, and MCA has an effect of promoting crystallization to some extent. Additionally, there are good synergistic effects between MCA and BPA-Zn, and the prepared PLA composites possess excellent flame retardancy. When the total mass fraction of BPA-Zn and MCA is 30% (mass ratio of BPA-Zn∶MCA=1∶1), the limit oxygen index of the composite is 28.0%, the vertical combustion flame retardant grade reaches V-0 grade and no droplets generate. 
关键词:聚乳酸;阻燃;苯基次磷酸锌;氰脲酸三聚氰胺 
Keywords:polylactic acid; flame retardant; zinc phenyl hypophosphite; melamine cyanurate 
本文引用格式:
张咪,丁晓庆,王克智,等.苯基次磷酸锌与MCA协效阻燃PLA的性能[J].工程塑料应用,2021,49(8):19-24.
Zhang Mi,Ding Xiaoqing,Wang Kezhi,et al. Performance of synergistic flame retardant PLA with zinc phenyl hypophosphite and MCA[J]. Engineering Plastics Application,2021,49(8):19-24. 

原文:
 
相似文章:
  PC/ABS/VMT/倍半硅氧烷阻燃性能研究
2021年第09期
  非APP无卤阻燃PP/充油SEBS弹性体材料研制
2021年第09期
  回收乙酸纤维素改性聚乳酸复合纤维制备及性能
2021年第09期
  连接器用玻纤增强阻燃PBT复合材料的结构与性能
2021年第09期
  室外自然老化对聚乳酸/茶渣材料结构与性能的影响
2021年第09期
  抗菌剂对高铁内饰用阻燃PC性能的影响
2021年第09期
  聚碳硅烷/双金属氢氧化物增强阻燃聚氨酯弹性体
2021年第09期
  医用聚乳酸材料改性方法及研究进展
2021年第08期
  透明耐热聚乳酸材料改性研究进展
2021年第08期
  不同溴系阻燃剂在阻燃ABS中燃烧行为与热行为
2021年第08期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878148 85878278
鲁ICP备05018524号-5