《工程塑料应用》 2022年第11期
DOI:10.3969/j.issn.1001-3539.2022.11.002
CF/MXene结构超级电容器的设计与性能
成丽媛,赵鑫,屈芸,秦佳音,孙洁
江南大学,江苏无锡 214000 
Design and Performance of CF/MXene Structural Supercapacitor
Cheng Liyuan, Zhao Xin, Qu Yun, Qin Jiayin, Sun Jie
Jiangnan University,Wuxi 214000,China 
摘要:为了制备出兼具力学承载和能量存储功能的结构超级电容器(结构超电)复合材料,首先采用二维纳米片状材料MXene对碳纤维(CF)进行表面改性,制备出高性能的CF/MXene复合纤维电极并将其组装成超级电容器,接着采用嵌入法将其排布在玄武岩纤维增强织物中,通过灌注环氧树脂共形固化制备结构超电复合材料。系统分析了CF/MXene超级电容器的耐温稳定性及其覆膜处理的影响作用,并对制得结构超电复合材料的综合性能进行全面考察。结果表明,采用聚二甲基硅氧烷(PDMS)对CF/MXene超级电容器进行覆膜处理,能有效保护其经受60℃持续12 h加热处理后的储能稳定性;组装的结构超电的密度为0.19 g/cm3,比电容可达3.38 mF/g (0.05 A/g),能量密度和功率密度分别为15.5 mWh/kg和256.4 mW/kg,其弯曲强度和弯曲弹性模量分别可达到199.6 MPa和4.54 GPa,且弯曲破坏后结构超电的电容保持率仍高达91%。整体上,制备的结构超电复合材料具备质轻、高强、储能性能优良且稳定的特点。 
Abstract:In order to prepare the structural supercapacitor composites with mechanical bearing and energy storage functions, MXene was firstly used to modify the surface of carbon fiber (CF), a high-performance CF/MXene composite fiber electrode was prepared and assembled into supercapacitor. Then, it was arranged in basalt fiber reinforced fabric by embedding method, and the structural supercapacitor composites were prepared by pouring resin to cure conformally. The temperature stability of CF/MXene supercapacitor and the effect of coating treatment were systematically analyzed, and the comprehensive properties of the prepared structural supercapacitor composites were comprehensively investigated. The results show that the use of polydimethylsiloxane (PDMS) to coat the CF/MXene supercapacitor can effectively protect the energy storage stability of the CF/MXene supercapacitor after being heated at 60℃ for 12 hours. The density of the structural supercapacitor composite is 0.19 g/cm3, the specific capacitance can reach 3.38 mF/g (0.05 A/g), and the energy density and power density are 15.5 mWh/kg and 256.4 mW/kg, respectively. Its bending strength and bending modulus can reach 199.6 MPa and 4.54 GPa respectively, and the capacitance retention rate of the structural supercapacitor after bending failure is still as high as 91%. On the whole, the prepared structural supercapacitor has the characteristics of light weight, high strength, excellent and stable energy storage performance. 
关键词:碳纤维;MXene;结构超级电容器;嵌入法;结构储能材料;电化学 
Keywords:carbon fiber; MXene; structural supercapacitors; embedded method; structural energy storage materials; electrochemistry 
基金:国家自然科学基金项目(51903109) 
本文引用格式:
成丽媛,赵鑫,屈芸,等.CF/MXene结构超级电容器的设计与性能[J].工程塑料应用,2022,50(11):8-16,73.
Cheng Liyuan,Zhao Xin,Qu Yun,et al. Design and performance of CF/MXene structural supercapacitor[J]. Engineering Plastics Application,2022,50(11):8-16,73. 

原文:
 
相似文章:
  CFRP在汽车轻量化中的应用研究进展
2022年第10期
  润滑剂对碳纤维增强PA66熔接线性能的影响
2022年第10期
  PEEK/CF成型用六自由度FDM3D打印系统设计及仿真
2022年第10期
  聚酰胺6/短切碳纤维复合材料制备及力学性能
2022年第10期
  碳纤维3D网络结构导热复合材料研究进展
2022年第09期
  拉挤成型碳纤维增强EP复合材料高低温力学性能
2022年第08期
  EP/CNTs-CF复合材料制备及工艺优化
2022年第07期
  硅烷偶联剂改性碳纳米管-碳纤维多尺度增强体表面
2022年第06期
  干湿环境对环氧树脂/碳纤维复合材料层合板老化性能的影响
2022年第04期
  变电站低压电缆绝缘层老化特征及老化模型
2022年第05期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878148 85878278
鲁ICP备05018524号-5